REF 100.01

Ferrite magnet AF01

Ferrite magnet

Isotropic or anisotropic ferrite magnets are brown stainless ceramics, obtained by powder metallurgy: pressing and sintering.

Ferrite is a hard but shock-sensitive material. The load-bearing capacity is optimal when the magnet is in contact with a clean, sufficiently thick, soft steel part. It decreases for alloyed steels (cast iron -30%), because of an air gap or because of a temperature rise (-0.4% per degree from 20°C).

Ferrite magnets cannot be machined, cut or drilled.
The assembly is done by gluing.

Magnet according to thickness

Use :
- ILS
- Relay
- Sensor
- Lock
- Clamping

Max. temperature of use :
- 200 °C
Density :
- 4.8 gr/cm³
Resistance in compression :
- 500 N/mm²
Max. surface induction :
- 1500 G

Product	Weight in kg	A	B	C
100.01-5x4	0.0005	5	4	0.82N
100.01-7x3	0.0007	7	3	1N
100.01-8x4	0.0008	8	4	1.7N
100.01-8x5	0.0012	8	5	1.8N
100.01-9x4	0.0015	9	4	2N
100.01-10x5	0.0022	10	5	3N
100.01-10x10	0.0044	1000	10	5N
100.01-12x5	0.0023	12	5	3.2N
100.01-14x4	0.003	14	4	3.6N
100.01-15x3	0.0022	15	3	3.5N
100.01-16x4	0.0032	16	4	3.8N
100.01-18x4	0.004	18	4	4N
100.01-18x5	0.0055	18	5	4.5N
100.01-20x5	0.007	20	5	5N
100.01-20x10	0.014	20	10	8N
100.01-23x3	0.003	23	3	4N
100.01-25x5	0.006	25	5	6N
100.01-25x10	0.012	25	10	10N
100.01-27x10	0.035	27	10	12N
100.01-28x6	0.022	28	6	10N
100.01-28x10	0.040	28	10	13N
100.01-30x5	0.020	30	5	10N
100.01-30x10	0.038	30	10	15N
100.01-30x15	0.064	30	15	25N
100.01-40x7	0.045	40	7	19N
100.01-40x10	0.060	40	10	25N
100.01-50x10	0.080	50	10	25N
100.01-56x12	0.150	56	12	29N
100.01-70x15	0.280	70	15	71N
100.01-110x21	0.920	110	21	100N